Material Status |
|
|
|
|
Literature 1 |
|
||
|
Availability |
|
|
|
|
Additive |
|
|
|
|
Features |
|
|
|
|
Uses |
|
|
|
|
Forms |
|
|
|
|
Processing Method |
|
|
|
|
Physical |
Nominal Value Unit |
Test Method |
|
|
Density |
0.918 g/cm³ |
ASTM D1505 |
|
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) |
2.0 g/10 min |
ASTM D1238 |
|
|
Mechanical |
Nominal Value Unit |
Test Method |
|
|
Tensile Stress |
|
JIS K6760 |
|
|
Yield |
12.0 MPa |
|
|
|
Break |
26.0 MPa |
|
|
|
Tensile Strain (Break) |
900 % |
JIS K6760 |
|
|
Apparent Bending Modulus |
260 MPa |
ASTM D747 |
|
|
Films |
Nominal Value Unit |
Test Method |
|
|
Film Thickness - Tested |
30 µm |
|
|
|
Tensile Modulus |
|
ISO IR 1184 |
|
|
MD : 30 µm |
190 MPa |
|
|
|
TD : 30 µm |
210 MPa |
|
|
|
Tensile Stress |
|
JIS Z1702 |
|
|
MD : Break, 30 µm |
40.0 MPa |
|
|
|
TD : Break, 30 µm |
35.0 MPa |
|
|
|
Tensile Elongation |
|
JIS Z1702 |
|
|
MD : Break, 30 µm |
600 % |
|
|
|
TD : Break, 30 µm |
900 % |
|
|
|
Dart Drop Impact (30 µm) |
110 g |
ASTM D1709 |
|
|
Elmendorf Tear Strength |
|
ASTM D1922 |
|
|
MD : 30 µm |
30 g |
|
|
|
TD : 30 µm |
140 g |
|
|
|
Hardness |
Nominal Value Unit |
Test Method |
|
|
Durometer Hardness (Shore D) |
54 |
ASTM D2240 |
|
|
Thermal |
Nominal Value Unit |
Test Method |
|
|
Brittleness Temperature |
< -70.0 °C |
ASTM D746 |
|
|
Vicat Softening Temperature |
100 °C |
ASTM D1525 |
|
|
Melting Temperature |
122 °C |
DSC |
|
Thông số kỹ thuật từ nhà sản xuất: Xem tại đây - LLDPE FD21HS